http://elartu.tntu.edu.ua/handle/lib/33044| Titel: | The Strength of the Adhesive Joints of the Medium-Density Fireboards and Particle Boards with the PVC Film |
| Författare: | Rudawska, Anna Stančeková, Dana Müller, Mirosław Vitenko, Tatiana Iasnii, Vlodymyr |
| Affiliation: | Ternopil Ivan Pulyui National Technical University Lublin University of Technology University of Žilina Czech University of Life Science Prague |
| Bibliographic description (Ukraine): | A. Rudawska, D. Stančeková, M. Müller, T. Vitenko, V. Iasnii. The Strength of the Adhesive Joints of the Medium-Density Fireboards and Particle Boards with the PVC Film. Adv. Sci. Technol. Res. J. 2020, 14(1):58–68 |
| Utgivningsdatum: | 1-mar-2020 |
| Date of entry: | 4-dec-2020 |
| Country (code): | PL |
| Nyckelord: | Manufacturing and Technology Mechanical Engineering adhesive joints strength MDF particle board PVC film |
| Page range: | 58-68 |
| Sammanfattning: | The aim of the present article was to analyse the adhesive joints of different types of the furniture boards used for the furniture production. The present article included a comparative analysis of the adhesive joints of the particle board and the medium-density fireboard (MDF) pressed with the following types of film: A 0.3 mm thick PVC film and a 0.8 mm thick acrylic film, made with use of a single-component reac-tive hot-melt adhesive based on the PUR 706.2 ME polyurethane. It was observed that, among others, the adhesive joints made of the particle board with a pressed 0.3 mm thick PVC film and the adhesive’s basis weight of 24 g/m2 is characterised by better strength properties than the adhesive joints of the particle board with the adhesive’s basis weight of 48 g/m2. |
| URI: | http://elartu.tntu.edu.ua/handle/lib/33044 |
| URL for reference material: | https://doi.org/10.12913/22998624/113612 |
| References (International): | Adams, R.D., Comyn, J., Wake ,W.C.: Structural Adhesive Joints in Engineering Book, 2nd edition, Springer, United Kingdom 1997. 2. Pizzi, A.: Advanced Wood Adhesive Technology, Marcel Dekker, New York, 1994. 3. Hass, P., Kläusler, O., Schlegel, S., Niemz, P.: Effects of mechanical and chemical surface preparation on adhesively bonded wooden joints. International Journal of Adhesion and Adhesives, 2014, 51:95–102. Rudawska, A.: Influence of the thickness of joined elements on lap length of aluminium alloy sheet bonded joints. Advances in Science and Technology Research Journal, 2015, Vol 9, no. 27, 35–44. Rudawska, A.: Pressure during curing and the strength of 2024, 2017A and 1050 aluminium alloy sheet adhesive joints. Advances in Science and Technology Research Journal, 2015, Vol 9, no. 26, 96 –103. Conrad, M.P.C., Smith, G.D., Fernlund, G.: Fracture of wood composites and wood-adhesive joints: A comparative review. Wood and Fibre Science, 2004, 1, 26–39. da Silva, L.F.M., Carbas, R.J.C., Critchlow, G.W., Figueiredo, M.A.V., Brown, K.: Effect of material, geometry, surface treatment and environment on the shear strength of single lap joints. International Journal of Adhesion and Adhesives, 2009, 29, 621–632. Bachtiar, E.V., Clerc, G., Brunner, A.J., Kaliske, M., Niemz, P.: Static and dynamic tensile shear test of glued lap wooden joint with four different types of adhesives, International Journal of the Biology, Chemistry, Physics, and Technology of Wood, 2017, 5, DOI: https://doi.org/10.1515/hf-2016–0154. Dunky, M.: Adhesives in the wood industry. In: Handbook of adhesive technology, revised and expanded, ed. A Pizzi, KL Mittal, Marcel Dekker, New York 2003. Selbo, M.L. Adhesive bonding of wood. Tech. Bull. 1512, 1975, Washington, DC: U.S. Department of Agriculture, Forest Service. Sellers, T. Jr.: Plywood and adhesive technology. Marcel Dekker, New York, 1985. Vick, C.B., Rowell, R.M.: Adhesive bonding of acetylated wood. International Journal of Adhesion and Adhesives, 1990, 10, 263–272. Serrano, E.: Adhesive Joints in Timber Engineering. Modelling and Testing of Fracture Properties. Division of Structural Mechanics, Lund University, LUND, Sweden, 2000. River, B.H.: Fracture of adhesive-bonded wood joints. In: Handbook of adhesive technology, revised and expanded, ed. A Pizzi, KL Mittal, Marcel Dekker, New York, 2003. Tankut, A.N., Tankut, N.: Evaluation the effects of edge banding type and thickness on the strength of corner joints in case-type furniture. Materials and Design, 2010, 31, 2956–2963 Frihart, Ch.R., Hunt, G.Ch.: Adhesives with Wood Materials Bond Formation and Performance, Chapter 10, General Technical Report FPL–GTR–190. https://www.fpl.fs.fed.us/documnts/fplgtr/fplgtr190/ chapter_10.pdf (available at 20.05.2019). Angelski, D., Vitchev, P.: Influences of some factors on adhesion strength between PVC foil and MDF. Processing Technologies for the Forest and Biobased Products Industries Conference, Rangava, H., Taghiyari, H.R., Ghofrani, M., Khojaste- Khosr, S.: Improving physical and mechanical properties in particleboard by recycled polyethylene and canola residues. International Journal of Environmental Science and Technology, 2016, 13, 857–864. Kociszewski, M.: Właściwości sprężyste płyty wiórowej i MDF jak materiałów anizotropowych o nierównomiernym rozkładzie gęstości na grubości płyty. Wydawnictwo Uniwersytetu Kazimierza Wielkiego, Bydgoszcz 2014. https://www.swisskrono.pl/mdm/Plyty-MDF/ Dane-techniczne (available at 20.05.2019). https://www.swisskrono.pl/mdm/Plyty-wiorowe/ Dane-techniczne (available at 20.05.2019). https://www.kleiberit.com/fileadmin/Content/Documents/ PL/Info_Sheets/PUR_Uebersicht_Prospekt_ PL.pdf (available at 20.05.2019). 23. https://admjacht.pl/public/assets//42-E53_KCh%20 PPE%2020.pdf (available at 20.05.2019). http://www.farbyjachtowe.pl/images/karty_techniczne/ sarzyna/kt_z1.pdf (available at 20.05.2019). |
| Content type: | Article |
| Samling: | Наукові публікації працівників кафедри будівельної механіки |
Fulltext och övriga filer i denna post:
| Fil | Beskrivning | Storlek | Format | |
|---|---|---|---|---|
| The Strength of the.pdf | 1,16 MB | Adobe PDF | Visa/Öppna |
Materialet i DSpace är upphovsrättsligt skyddat och får ej användas i kommersiellt syfte!
Administrativa verktyg