Title: | Корозійна деградація сталей сітчастих гіперболоїдних конструкцій |
Other Titles: | Corrosion degradation of steels of the lattice hyperboloid constructions |
Authors: | Кутний, А. Никифорчин, Григорій Миколайович Zvirko, O. Kutnyi, A. Nykyforchyn, H. |
Bibliographic description (Ukraine): | Звірко О. Корозійна деградація сталей сітчастих гіперболоїдних конструкцій / О. Звірко, А. Кутний, Г. Никифорчин // Вісник ТНТУ — Тернопіль : ТНТУ, 2013. — Том 72. — № 4. — С 36-42. — (механіка та
матеріалознавство). Zvirko O. Corrosion degradation of steels of the lattice hyperboloid constructions / O. Zvirko, A. Kutnyi, H. Nykyforchyn // Bulletin of TNTU — Ternopil : TNTU, 2013. — Volume 72. — No 4. — P 36-42. — (mechanics and materials science). |
Issue Date: | 19-nov-2013 |
Date of entry: | 3-sze-2014 |
Publisher: | Тернопiльський національний технiчний унiверситет iменi Iвана Пулюя |
Place of the edition/event: | Тернопіль |
UDC: | 620.193 |
Keywords: | вуглецева сталь вежа Шухова корозійна тривкість електрохімічні характеристики деградація carbon steel Shukhov tower corrosion resistance electrochemical properties degradation |
Abstract: | Досліджено корозійну тривкість та електрохімічну поведінку вуглецевих сталей
експлуатованих понад 100 років сітчастих гіперболоїдних конструкцій (веж Шухова) та сучасної
вуглецевої сталі у вихідному стані у 0,3% водному розчині NaCl. Встановлено, що вуглецева сталь
Аджигольського маяка характеризується нижчою корозійною тривкістю порівняно з сучасною
вуглецевою сталлю у вихідному стані та вуглецевою сталлю водонапірної вежі у Черкасах, що зумовлено
тривалим впливом агресивного корозивного наводнювального середовища. Виявлено погіршення низки
корозійно-електрохімічних характеристик сталі маяка внаслідок її експлуатаційної деградації –
стаціонарного потенціалу, густини струму корозії та поляризаційного опору, які можуть виступати
достатньо чутливими інформаційними ознаками експлуатаційної деградації сталі. A number of unique engineering monuments – the lattice towers created by outstanding engineer V.G. Shukhov have been preserved in Ukraine. Atmospheric corrosion is the main reason of the deterioration of their performance because the towers are made of carbon steel, which has insufficient corrosion resistance and they are not properly protected against corrosion. Therefore, the expertise of constructions corrosion damages, the establishment of corrosion peculiarities, the use of modern corrosion protection and corrosion monitoring are necessary for their conservation. The paper is devoted to studying the influence of long-term operation on corrosion resistance and electrochemical behavior of carbon steels of lattice hyperboloid towers in comparison with modern carbon steel in the initial state and detecting the informative features, which are sensitive to a change of a metal state due to long-term operation. The corrosion resistance and electrochemical behavior of carbon steels of the 100-year-old Shukhov lattice towers and modern carbon steel in the initial state in 0.3% NaCl aqueous solution have been investigated. It has been established that the Adziogol Lighthouse carbon steel is characterized by the reduced corrosion resistance in comparison with the modern carbon steel in the initial state and the carbon steel of the Cherkasy water tower which is likely to be caused by long-term exposure to aggressive corrosive and hydrogenating environment. The deterioration of corrosion and electrochemical properties of lighthouse steel, such as stationary potential, corrosion current density and polarization resistance, due to its exploited degradation has been found. These characteristics may be enough informative features of the in-service steel degradation. To maintain a conservation of the lattice tower constructions it is necessary to provide its effective corrosion protection using modern technology. |
URI: | http://elartu.tntu.edu.ua/handle/123456789/3379 |
ISSN: | 1727-7108 |
Copyright owner: | © „Вісник Тернопільського національного технічного університету“ |
Content type: | Article |
Ebben a gyűjteményben: | Вісник ТНТУ, 2013, № 4 (72) |
Fájlok a dokumentumban:
Fájl | Leírás | Méret | Formátum | |
---|---|---|---|---|
TNTUB_2013v72n4_O_Zvirko-Corrosion_degradation_of_steels_36-42.pdf | 332,29 kB | Adobe PDF | Megtekintés/Megnyitás | |
TNTUB_2013v72n4_O_Zvirko-Corrosion_degradation_of_steels_36-42.djvu | 326,23 kB | DjVu | Megtekintés/Megnyitás | |
TNTUB_2013v72n4_O_Zvirko-Corrosion_degradation_of_steels_36-42__COVER.png | 154,92 kB | image/png | Megtekintés/Megnyitás |
Minden dokumentum, ami a DSpace rendszerben szerepel, szerzői jogokkal védett. Minden jog fenntartva!